Acoustic Assessment of Microstructural Deformation Mechanisms on a Cold Rolled Cu30Zn Brass

The relationship between acoustic parameters and the microstructure of a Cu30Zn brass plate subjected to plastic deformation was evaluated. The plate, previously annealed at 550 degrees C for 30 min, was cold rolled to reductions ranging from 10% to 70%.